Manufacturer of Forgings and Superalloys



QN625 (UNS N06625)




Chemical Composition

C

Si

Mn

P

S

Ni

Cr

Mo

Al

TI

Fe

Co

Nb

Min

58.0

20.0

8.0

3.15

Max

0.01

0.50

0.50

0.015

0.015

23.0

10.0

4.0

4.0

5.0

1.0

4.15




Physical Properties

Specific heat (J/kgK)

410

Specific resistivity (μΩcm)

1.29

Thermal conductivity (W/mK)

9.8

Coefficient of thermal expansion (10-6/)

20–100

12.8

Young's modulus (MPa)

20.4 x 104

Modulus of rigidity (MPa)

78.8 x 104

Ferromagnetism

None

Melting point ()

1290-1350




Mechanical Properties


ASTM B443 Grade 1 / UNS N06625 (annealed)

0.2% proof stress
(N/mm2)

Tensile strength
(N/mm2)

Elongation
(%)

Hardness
(HRB)

Cold-rolled sheet,
strip

≥ 414

≥ 827

≥ 30

Hot-rolled sheet,
≤ 70mm

≥ 379

≥ 758

≥ 30

Cold-rolled sheet,
≤ 9.5mm

≥ 379

≥ 758

≥ 30


ASTM B443 Grade 2 / UNS N06625 (solution treated)

0.2% proof stress
(N/mm2)

Tensile strength
(N/mm2)

Elongation
(%)

Hardness
(HRB)

≥ 276

≥ 690

≥ 30

 


Disclaimer: The data given on this page is for general reference only and should not be treated as the standard requirements. Different specifications of the same material grade might have different requirements. Buyer is advised to review the appropriate specifications before placing an order for the material. QSC Forge is not responsible or liable for any errors.